Lukachrom C

Composition                                  
Co    63,0 %                                                    
Cr    24,0 %              
Mo    3,0 %                                                
W    8,0 %                                                     
Nb    1,0 %                                                
Si    1,0 %                                                     
other Metals    < 1 %                               
                                                                                              

Technical Details:
Type    NPA-for ceramics
Vickers-Hardness    280 HV 10
Tensile Strenght N/mm²    550 MPa

Elastic-Modulus N/mm²    210 GPa
Elongation in %    10 %
Density    8,3 g/qcm

Solidus    1.304° C
Liquidus    1.369° C
CTE Value    (25-500° C)    13,9 µm/m.k
                   (25-600° C)    14,0 µm/m.k